The X65Q PSL2 steel pipe strictly complies with the PSL2 requirements of API SPEC 5L 46th Edition (Steel pipes for pipeline transportation systems in the petroleum and natural gas industries), covering core indicators such as chemical composition, tensile properties, and impact testing. The X65Q pipes supplied by GNEE Group undergo 100% ultrasonic testing (UT), radiographic inspection (RT), and hydrostatic testing to ensure defect-free delivery.
Dimension:
1)seamless OD:21.3-508mm WT:2-60mm
2)HFW/ERW OD:21.3-508mm WT:3.2-15.9mm
3)LSAW OD:406.4-1422mm WT:6.4-44.5mm
4)SSAW OD:219.1-2540mm WT:5.4-25.4mm
API 5L X65Q PSL2 welded/ seamless pipes Chemical composition:
|
Grade |
PSL |
Chemical Composition weight% , Max |
||||
|
C |
Si |
Mn |
P |
S |
||
|
X65Q |
PSL2 |
0.18 |
0.45 |
1.70 |
0.025 |
0.015 |
API 5L X65Q PSL2 Mechanical properties:
|
Grade
|
PSL
|
Yield Strength
|
Tensile Strength
|
Elongation % Min |
||
|
Min |
Max |
Min |
Max |
|||
|
X65Q |
PSL2 |
450 MPa (65300 PSI) |
600 MPa (87000 PSI) |
535 MPa (77600 PSI) |
760 MPa (110200 PSI) |
1940*A2/U0.9 |
Note:
A-Cross sectional area of the tensile test specimen.(mm)
U-Specified minimum ultimate tensile strength in MPa.
API 5L X65Q PSL2 Charpy impact test:
|
Grade |
Absorbed Energy J 10x10x55 T-10-27 |
|||
|
Average |
Individual Specimen |
|||
|
Longitudinal |
Transverse |
Longitudinal
|
Transverse |
|
|
X65Q |
- |
≥27J |
- |
≥20J |
Note :
1. The test temperature is 0℃.
2. The axis of the notch shall be perpendicular to the pipe surface.
Heat treatment：
All pipes shall be Quenched and Tempered according to a documented procedure.